Zhou, S; Assassa, Y-J; Cowe, B; Marchebois, H; Kairy, S K; Turnbull, A (2025) Effect of Filler Metal Chemistry on Preferential Weld Corrosion in Hydrocarbon and Produced Water Service Using the Galvanostatic Method. Corrosion, 81 (2). pp. 194-202. ISSN 0010-9312

Full text not available from this repository.

Abstract

The effect of Ni content in weld consumables on the preferential weld corrosion (PWC) of welded pipeline steel for hydrocarbon and produced water service has been investigated using the galvanostatic method as a preliminary assessment tool. The method involves the application of a modest anodic current to the weldment over a short period, in this case, 62 h. The distribution of material loss and the extent of PWC is then characterized by 3D profiling. Testing was conducted for 0% Ni, 1% Ni, and 2% Ni weld fillers in 50 g/L NaCl at 60°C with 1 bar CO2. For these sweet environments, the results demonstrate an increased resistance to corrosion of the weld metal and heat-affected zone (HAZ) for the Ni-weld filler, compared to the weld metal free of Ni and the parent steel. However, for all weldments, the fusion zone and HAZ/parent steel interface were more prone to attack than the parent steel, albeit the addition of Ni reduced the extent of corrosion at the fusion zone.

Item Type:	Article
Keywords:	galvanostatic method, hydrocarbon pipelines, Ni-weld consumable, preferential weld corrosion
Subjects:	Advanced Materials > Corrosion
Divisions:	Electromagnetic & Electrochemical Technologies
Identification number/DOI:	10.5006/4636